Antifriction coating MC 2020

Antifriction coating MC 2020

The composition MC 2020 is a suspension of molybdenum disulfide in a polymer solution and is designed to obtain an anti-friction solid lubricant coating cured at room temperature.

Antifriction coating MC 2020

Antifriction coating MC 2020

WHERE TO BUY

Packing: 20 g

Code: 1703

About
Instruction
Where to buy

Advantages

  1. Prevents parts from seizing.
  2. Promotes smooth operation of friction units and facilitates running-in.
  3. It has a high bearing capacity – an increased resource of the friction pair.
  4. Effectively protects against corrosion.
  5. Improves performance in dusty and humid environments.
  6. Frost and heat resistance: from -50 ° C to + 200 ° C.
  7. Has performance in a vacuum.
  8. High adhesion – adheres well to the surface.
Prevents parts from seizing

Prevents parts from seizing

Surface preparation

The surface must be thoroughly cleaned, degreased using solvent 646 or nefras C2-80 / 120, then dried. It is recommended to dry it in an oven or drying cabinet at a temperature of about + 50 ° C for 30 minutes.

Contamination of the prepared surface with water, oil, dust, other substances that can reduce the adhesion of the composition to the substrate is not allowed, contact with hands is not allowed. The interval between the operation of surface preparation and the application of MC 2020 should not exceed 60 minutes.

The durability of the coating depends on the surface roughness, the optimal value of which is Ra = 1.6-3.2 microns. Preliminary sandblasting and chemical surface treatment are recommended.

Application

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes (non-uniformity of color is allowed with stirring). At the end of mixing, the composition should be a dark gray-colored mass, while no sediment should remain on the bottom and on the walls of the container. If necessary, dilution of MS 2020 with technical isopropyl alcohol is allowed.

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes

Application of the composition is recommended at a temperature of 20 ± 10 ° C and relative humidity of no more than 80% by one of the following methods:

Spraying

It is the most preferable since it allows you to control the thickness and uniformity of the applied layer. Provides maximum adhesion and wear resistance of the coating.

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes

Dipping

Not recommended for assemblies where thickness control is required.

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes

Brush application

Not recommended for assemblies where thickness control is required.

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes

The composition of MS 2020 is applied in 1-2 layers. The recommended dry layer thickness is 7-15 microns. If necessary, the second layer is applied after drying the previous one in air at room temperature until matt appears (20 minutes). The surface should be covered as evenly as possible.

Curing
The part with the applied composition is dried in air at a temperature of 15 ÷ 25 ° C for 2-3 hours, after which it can be put into operation.

It is recommended to control the thickness of the coating with a thickness gauge for paints and varnishes. If the thickness of the coating is greater than the required one, it is allowed to fine-tune the specified thickness by lapping with the mating part. Abrasive cleaning is prohibited.

Quality control

Upon visual inspection, the coating should be matt, solid and dark gray. Bubbles, drips, delamination, foreign inclusions, craters, gloss, mechanical damage are not allowed.

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes

Stir the composition of MC 2020 thoroughly before use with a clean stick or stirrer for at least 10 minutes

NOTE!

Since the conditions and methods of using MC 2000 in each specific case are not under the control of VMPAUTO LLC, if you have any questions or difficulties, please contact us by phone: +7 (812) 601 05 53 or email: export@vmpauto.com

VMPAVTO LLC guarantees only compliance with MC 2000 during manufacture. The use of MC 2000 is possible only on serviceable parts and only in those cases when it does not contradict the design and operational documentation for a friction pair.